Fin structure of fin field effect transistor

ABSTRACT

An exemplary method of forming a fin field effect transistor that includes first and second etching processes to form a fin structure. The fin structure includes an upper portion and a lower portion separated at a transition. The upper portion has sidewalls that are substantially perpendicular to the major surface of the substrate. The lower portion has tapered sidewalls on opposite sides of the upper portion and a base having a second width larger than the first width.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a continuation application of U.S. application Ser. No. 12/766,233, filed Apr. 23, 2010, issuing as U.S. Pat. No. 9,484,462, titled FIN STRUCTURE OF FIN FIELD EFFECT TRANSISTOR, which claims priority of U.S. Provisional Patent Application Ser. No. 61/245,485, filed on Sep. 24, 2009. The disclosures of each of which are incorporated by reference in their entirety.

In addition, this application is also related to U.S. patent application Ser. Nos. 12/707,788, filed on Feb. 18, 2010, (Docket Nos. TSMC2008-0432, T5057-R007U), titled MEMORY POWER GATING CIRCUIT AND METHODS; 12/758,426, filed on Apr. 12, 2010, (Docket Nos. TSMC2008-0582, T5057-Y048U), titled FINFETS AND METHODS FOR FORMING THE SAME; 12/731,325, filed on Mar. 25, 2010, (Docket Nos. TSMC2008-0597, T5057-B033U), titled ELECTRICAL FUSE AND RELATED APPLICATIONS; 12/724,556,filed on Mar. 16, 2010, (Docket Nos. TSMC2008-0598, T5057-K002U), titled ELECTRICAL ANTI-FUSE AND RELATED APPLICATIONS; 12/757,203, filed on Apr. 9, 2010, (Docket Nos. TSMC2009-0148, T5057-Y085U), titled STI STRUCTURE AND METHOD OF FORMING BOTTOM VOID IN SAME; 12/797,839, filed on Jun. 10, 2010, (Docket Nos. TSMC2009-0278, T5057-K099U), titled FIN STRUCTURE FOR HIGH MOBILITY MULTIPLE-GATE TRANSISTOR; 12/831,842, filed on Jul. 7, 2010, (Docket Nos. TSMC2009-0343, T5057-Y093U), titled METHOD FOR FORMING HIGH GERMANIUM CONCENTRATION SiGe STRESSOR; 12/761,686, filed on Apr. 16, 2010, (Docket Nos. TSMC2009-0442, T5057-Y125U), titled FINFETS AND METHODS FOR FORMING THE SAME; 12/766,233, filed on Apr. 23, 2010, (Docket Nos. TSMC2009-0445, T5057-Y113U), titled ACCUMULATION TYPE FINFET, CIRCUITS AND FABRICATION METHOD THEREOF; 12/694,846, filed on Jan. 27, 2010, (Docket Nos. TSMC2009-0646, T5057-Y165), titled INTEGRATED CIRCUITS AND METHODS FOR FORMING THE SAME; 12/638,958, filed on Dec. 14, 2009, (Docket Nos. TSMC2009- 0738, T5057-B166), titled METHOD OF CONTROLLING GATE THICKNESS IN FORMING FINFET DEVICES; 12/768,884, filed on Apr. 28, 2010, (Docket Nos. TSMC2010-0028, T5057-Y228), titled METHODS FOR DOPING FIN FIELD-EFFECT TRANSISTORS; 12/731,411, filed on Mar. 25, 2010, (Docket Nos. TSMC2010-0057, T5057-B218), titled INTEGRATED CIRCUIT INCLUDING FINFETS AND METHODS FOR FORMING THE SAME; 12/775,006, filed on May 6, 2010, (Docket Nos. TSMC2010-0198, T5057-Y246), titled METHOD FOR FABRICATING A STRAINED STRUCTURE; 12/886,713, filed Sep. 21, 2010, (Docket Nos. TSMC2010-0646, T5057-B325), titled METHOD OF FORMING INTEGRATED CIRCUITS; 12/941,509, filed Nov. 8, 2010, (Docket Nos. TSMC2010-0561, T5057-B337), titled MECHANISMS FOR FORMING ULTRA SHALLOW JUNCTION; 12/900,626, filed Oct. 8, 2010, (Docket Nos. TSMC2010-0581, T5057-B330), titled TRANSISTOR HAYING NOTCHED FIN STRUCTURE AND METHOD OF MAKING THE SAME; 12/903,712, filed Oct. 13, 2010, (Docket Nos. TSMC2010-0731, T5057-R350), titled FINFET AND METHOD OF FABRICATING THE SAME; 61/412,846, filed Nov. 12, 2010, (Docket Nos. TSMC2010-0839, T5057-B388PRO), 61/394,418, filed Oct. 19, 2010, (Docket Nos. TSMC2010-0926, T5057-Y351PRO), titled METHODS OF FORMING GATE DIELECTRIC MATERIAL and 61/405,858, filed Oct. 22, 2010, (Docket Nos. TSMC2010-0928, T5057-R368PRO), titled METHODS OF FORMING SEMICONDUCTOR DEVICES, which are incorporated herein by reference in their entirety.

TECHNICAL FIELD

The present invention relates generally to transistors, and more particularly to a fin field effect transistor with an isolation structure.

BACKGROUND

Semiconductor devices are used in a large number of electronic devices, such as computers, cell phones, and others. Semiconductor devices comprise integrated circuits (ICs) that are formed on semiconductor wafers by depositing many types of thin films of material over the semiconductor wafers, and patterning the thin films of material to form the integrated circuits. The ICs include field-effect transistors (FETs), such as metal-oxide-semiconductor field-effect transistors (MOSFETs).

One of the goals of the semiconductor industry is to continue shrinking the size and increasing the speed of individual MOSFETs. To achieve these goals, three dimensional (3-D) or non-planar transistor structures such as fin FETs (FINFETs), multiple gate transistors, or gate-all-around transistors are being investigated for use in sub 22 nm transistor nodes. Such transistors not only improve area density, but also improve gate control of the channel.

However, fabrication of the FINFETs is complex and requires overcoming a number of challenging problems. One of the challenges is forming recess-free isolation structures. These recesses can be formed in a dielectric material in the early stages of forming the isolation structure. FIGS. 1A-C show cross-sectional views of a plurality of conventional isolation structures 120 for FINFETs 100 having recesses 126 b present in the isolation structures 120 at various stages of fabrication. FIG. 1A illustrates the plurality of isolation structures 120 may be formed by etching a substrate 102 to form a plurality of trenches 122 separating a plurality of fin structures 110, then filling the plurality of trenches 122 with a dielectric material 124 (shown in FIG. 1B), such as high-density plasma (HDP) oxides, tetraethoxysilane (TEOS) oxides, or the like. The dielectric material 124 may comprise a plurality of deep slims/recesses 126 a due to the high aspect ratio of the plurality of trenches 122. FIG. 1C shows a plurality of recesses 126 b in the plurality of isolation structures 120 may be formed along the plurality of deep slims/recesses 126 a during and after removing the upper portions of the dielectric material 124. The plurality of recesses 126 b is problematic in various respects. For example, the plurality of recesses 126 b present in the plurality of isolation structures 120 can become a receptacle of polysilicon and/or metals during subsequent processing thereby increasing the likelihood of device instability and/or device failure.

Accordingly, what is needed is an isolation structure for a FINFET having no recess.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure is best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, various features are not drawn to scale and are used for illustration purposes only. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIGS. 1A-C show cross-sectional views of a plurality of conventional isolation structures for FINFETs having recesses present in the isolation structures at various stages of fabrication;

FIGS. 2A-H show schematic cross-sectional views of a substrate being processed to fabricate a plurality of FINFETs according to an embodiment, showing various stages of fabrication;

FIG. 2I shows a perspective view of the plurality of the FINFETs fabricated using the steps shown in FIG. 2A-H; and

FIG. 3A-D shows a complete FINFET device having a plurality of isolation structures fabricated using the steps shown in FIG. 2A-H, wherein FIG. 3A shows a perspective view, and wherein FIGS. 3B-D show cross-section views taken along the respective lines of FIG. 3A.

DESCRIPTION

It is understood that the following disclosure provides many different embodiments, or examples, for implementing different features of the invention. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed. Various features may be arbitrarily drawn in different scales for the purpose of simplicity and clarity.

FIGS. 2A-H show schematic cross-sectional views of a substrate being processed to fabricate a plurality of FINFETs according to an embodiment, showing various stages of fabrication, and FIG. 2I shows a perspective view of the plurality of the FINFETs fabricated using the steps shown in FIG. 2A-H. It is understood that part of the FINFETs 200 may be fabricated with normal complementary metal-oxide-semiconductor (CMOS) technology processes, and thus some processes are briefly described herein. Also, FIGS. 2A-H are simplified for a better understanding of the inventive concepts of the present disclosure. For example, although the figures illustrate the FINFET 200, it is understood the ICs may also include a number of various devices including resistors, capacitors, inductors, fuses, etc.

Referring to FIG. 2A, the FINFETs 200 may include a semiconductor substrate 202 such as a silicon substrate. In some embodiments, the substrate 202 may alternatively include silicon germanium, gallium arsenic, or other suitable semiconductor materials. The substrate 202 may further include other features such as various doped regions, a buried layer, and/or an epitaxy layer. Furthermore, the substrate 202 may be a semiconductor on insulator such as silicon on insulator (SOI). In other embodiments, the semiconductor substrate 202 may include a doped epi layer, a gradient semiconductor layer, and/or may further include a semiconductor layer overlying another semiconductor layer of a different type such as a silicon layer on a silicon germanium layer. In other examples, a compound semiconductor substrate 202 may include a multilayer silicon structure or a silicon substrate 202 may include a multilayer compound semiconductor structure.

Still referring to FIG. 2A, a pad oxide layer 204 is formed over the top surface of the substrate 202. In some embodiments, the pad oxide layer 204 is preferably formed of silicon oxide grown by a thermal oxidation process, having a thickness of about 80 to 150 A. For example, the pad oxide layer 204 can be grown by the rapid thermal oxidation (RTO) process or in an annealing process, which include oxygen. A hardmask layer 206, for example a silicon nitride or silicon oxynitride layer, is formed over the pad oxide layer 204. The hardmask layer 206 can be deposited by, for example, a chemical vapor deposition (CVD) process, or a low pressure CVD (LPCVD) process. Preferably, in some embodiments, the formed hardmask layer 206 has a thickness of about 600 to 1500 Å.

Referring to FIG. 2B, following formation of the hardmask layer 206, a patterned photo-sensitive layer (not shown) is formed on the hardmask layer 206. A reactive ion etching (ME) or a high density plasma (HDP) process may, for example, be used to anisotropically etch through the hardmask layer 206 and the pad oxide layer 204 to form openings 208 in the hardmask layer 206 and the pad oxide layer 204, exposing a portion of the substrate 202.

Referring to FIG. 2C, upper portions 210 a of a plurality of fin structures 210 protruding from the major surface 202 a of the substrate 202 may be formed by etching the substrate 202 using a first etch process. For example, the first etch process may be performed under a source power of about 550 to 650 W, a bias power of about 55 to 65 W, and a pressure of about 2 to 10 mTorr, using CH2F2, SF6, N2, and He as etching gases. The substrate 202 comprises a major surface 202 a parallel to a substrate surface 202 b. The upper portion 210 a of each fin structure 210 has sidewalls that are substantially perpendicular to the major surface 202 a of the substrate 202 and a top surface 210 c.

Referring to FIG. 2D, lower portions 210 b of the plurality of fin structures 210 protruding from the major surface 202 a of the substrate 202 may be formed by further etching the substrate 202 using a second etch process. For example, the second etch process may be performed under a source power of about 1100 to 1250 W, a bias power of about 200 to 220 W, and a pressure of about 10 to 20 mTorr, using HBr, SF6, and He as etching gases. The upper portion 210 a and the lower portion 210 b of each fin structure 210 are separated at a transition location 210 d at, in some embodiments, where the sidewall of the fin structure at an angle 212 of 85 degrees to the major surface 202 a of the substrate 202. The lower portion 210 b of each fin structure 210 has tapered sidewalls on opposite sides of the upper portion 210 a and a base 210 e. In some embodiments, the tapered regions of the lower portion 210 b of each fin structure 210 is preferably at an angle 214 in the range of 60 degrees to 85 degrees to the major surface 202 a of the substrate 202. In one embodiment, a plurality of trenches 222 formed between the tapered fin structures 210 have lower aspect ratio than the plurality of trenches 122 formed between the vertical fin structures 110. The lower aspect-ratio trenches 222 have better gap-fill performance than the higher aspect-ratio trenches 122.

Still referring to FIG. 2D, the top surface 210 c of the upper portion 210 a of each fin structure 210 having a first width 216 a, the first width 216 a is in the range of about 5 to 40 nanometers. In one embodiment, the base 210 e of the lower portion 210 b of each fin structure 210 having a second width 218 a, the second width 218 a is in the range of about 10 to 60 nanometers. In some embodiments, a ratio of the first width 216 a to the second width 218 a is preferably from 0.3 to 0.5.

Still referring to FIG. 2D, in some embodiments, a first offset distance 216 b between the transition location 210 d and the top surface 210 c is in the range of about 40 to 100 nanometers. In some embodiments, a second offset distance 218 b between the base 210 e and the top surface 210 c is in the range of about 100 to 300 nanometers. A ratio of the first offset distance 216 b between the transition location 210 d and the top surface 210 c to the second offset distance 218 b between the base 210 e and the top surface 210 c, in some embodiments, is preferably from 0.15 to 0.3.

Referring to FIG. 2E, following formation of the plurality of the fin structures 210, the plurality of the isolation structures 220 between the fin structures 210 may be formed in the plurality of the trenches 222. In some embodiments, a liner layer (not shown) may be formed substantially conformal over the substrate 202, including along the sidewalls of the plurality of the trenches 222. The liner layer is a dielectric layer (e.g., an oxide layer, nitride layer, oxynitride layer or combination thereof) formed by a thermal oxidation process or CVD process. Preferably, the liner layer may have a thickness of about 30 to 200 Å. In some embodiments, the liner layer is provided for reducing damage on the surface of the fin structures 210 created by the trench-etch process as set forth above. In some embodiments, the liner layer is not used.

Still referring to FIG. 2E, following formation of the liner layer, a dielectric material 224 is formed over the liner layer to a sufficient thickness within and above the plurality of the trenches 222. For example, the dielectric material 224 is preferably deposited to a thickness from the base 210 e of 4000 to 8000 Å. In one embodiment, the dielectric material 224 can be formed using a CVD process, such as HDP CVD process or sub-atmospheric CVD (SACVD) process. For example, the dielectric material 224 comprises HDP-CVD oxide layer. The dielectric material 224 can be deposited under a low frequency power less than 5000 W, a high frequency power less than 3500 W, a pressure less than 10 mTorr and a temperature of about 500 to 1000° C., using silane and oxygen as reacting precursors. For another example, the dielectric material 224 comprises a sub-atmospheric undoped-silicon glass (SAUSG) layer. The dielectric material 224 can be deposited under a pressure of about 500 to 700 torr and a temperature of about 500 to 600° C., using tetraethoxysilane (TEOS) and O₃ as reacting precursors. The dielectric material 224 may comprise a plurality of shallow slims/recesses 226 a due to reduced aspect ratio of the plurality of trenches 222.

Still referring to FIG. 2E, following formation of the dielectric material 224 within and above the plurality of trenches 222, an annealing process is performed to increase the density of the dielectric material 224. This results in an interface between the liner layer and the dielectric material 224 that will disappear after the anneal process. The anneal process can be performed, for example, in a furnace, a rapid thermal process (RTP) system or other thermal system that is adapted to provide a thermal treatment for the dielectric material 224 to obtain a desired film quality. In some embodiments, the annealing process may be performed at about 1000° C. for about 20 seconds in a RTP system in an environment containing nitrogen, an inert gas or other gas that will not substantially react with the dielectric material 224.

FIG. 2F shows the substrate 202 of FIG. 2E after a planarization process, such as a chemical mechanical polishing (CMP) process, is performed to remove portions of the dielectric material 224 above the hardmask layer 206 to expose the hardmask layer 206, thereby leaving the dielectric material 224 filling the trenches 222. The hardmask layer 206 also serves as a stop layer for stopping the planarization process on the hardmask layer 206. In some embodiments, a top surface of the dielectric material 224 is or substantially coplanar with the hardmask layer 206. The plurality of the shallow slims 226 b of the dielectric material 224 after the planarization process may become even shallower in depth and broader in width than the plurality of shallow slims 226 a of the dielectric material 224 before the planarization process.

Referring to FIG. 2G, after the planarization process, the hardmask layer 206 has been removed by a wet chemical etching process, for example, by dipping the substrate 202 in hot phosphoric acid (H₃PO₄), exposing a top surface of the pad oxide layer 204. Because the wet chemical etching process has higher etch selectivity for nitride than to oxide, the etch process removes the hardmask layer 206 faster than the dielectric material 224. Accordingly, the remaining dielectric material 224 extends over a top surface of the pad oxide layer 204. Subsequent to the hardmask layer 206 removal process, the pad oxide layer 204 has been removed by a wet etching process, for example, by dipping the substrate 202 in hydrofluoric (HF), exposing the top surface of the substrate 202. Since the wet chemical etching process has almost no selectivity for the pad oxide layer 204 and the dielectric material 224, the dielectric material 224 may lose almost the same thickness as the pad oxide layer 204 does. Accordingly, the dielectric material 224 still protrudes over the top surface 210 c of each fin structure 210 and each shallow slim recess 226 c in the dielectric material 224 almost disappear.

FIG. 2H shows the substrate 202 of FIG. 2G after a dry etching process, for example, by etching the substrate 202 in a plasma comprising tetrafluormethane (CF4) and trifluormethane (CHF3), is performed to remove upper portions of the dielectric material 224 to expose the upper portion 210 a of each fin structure 210. The fin structure could also form part of other devices, such as resistors, capacitors, inductors, fuses, etc. Accordingly, at the end of the etching process, the dielectric material 224 made has almost no recess and serves as the isolation structures 220 between the semiconductor devices. Each isolation structure 220 extends from the substrate surface 202 a to a point 224 a above the transition location 201 d. A third offset distance 216 c between the point 224 a of the isolation structure 220 and the top surface 210 c should be well controlled. If the third offset distance 216 c between the point 224 a of the isolation structure 220 and the top surface 210 c is too small, shallow slims/recesses may still remain on the point 224 a of the isolation structure 220. If the third offset distance 216 c between the point 224 a of the isolation structure 220 and the top surface 210 c is too large, short channel effects may degrade device performance. Accordingly, in some embodiments, the third offset distance 216 c between the point 224 a of the isolation structure 220 and the top surface 210 c is preferably in the range of about 15 to 45 nanometers. In some embodiments, the ratio of the third offset distance 216 c between the point 224 a of the isolation structure 220 and the top surface 210 c to the first offset distance 216 b between the transition location 210 d and the top surface 210 c to is preferably from 0.3 to 0.6. FIG. 21 shows a perspective view of the FINFETs 200 fabricated using the steps shown in FIG. 2A-H. Each fin structure 210 extends in a longitudinal direction 210 g. As previously described the isolation structure 220 in FIG. 21 has no recesses.

FIG. 3A-D shows a complete FINFET device 300 having a plurality of isolation structures 220 fabricated using the steps shown in FIG. 2A-H, wherein FIG. 3A shows a perspective view, and wherein FIGS. 3B-D show cross-section views taken along the respective lines of FIG. 3A. Similar features in FIGS. 2 and 3 are numbered the same for the sake of simplicity and clarity.

Referring to FIG. 3A, the FINFET 300 includes the plurality of fin structures 210 separated by the plurality of isolation structures 220. Each fin structure 210 extends in a longitudinal direction 210 g. A gate structure 320 comprising a gate electrode 320 a and a gate insulator 320 b is disposed over the fin structures 210. FIG. 3A also illustrates the source/drain regions 330 a, 330 b, 329 a and 329 b of the FINFET 300.

FIG. 3B illustrates a cross-sectional view of the FINFET 300 taken along the line b-b of FIG. 3A. Each fin structure 210 extending in a longitudinal direction 210 g comprises an upper portion 210 a and a lower portion 210 b separated at a transition location 210 d at where the sidewall of the fin structure 210 at an angle of 85 degrees to the major surface 202 a of the substrate 202, the upper portion 210 a has sidewalls that are substantially perpendicular to the major surface 202 a of the substrate 202 and a top surface 210 c, the upper portion 210 a comprises a first longitudinal portion 210 ga, a second longitudinal portion 210 gb, and a third longitudinal portion 210 gc disposed between the first and the second longitudinal portions 210 ga, 219 gb. A channel region 330 is defined within the third longitudinal portion 210 gc of the upper portion 210 a. A gate structure 320 comprising a gate electrode 320 a and a gate insulator 320 b may be disposed over the channel region 330. A silicide layer (not shown) may be disposed within the first and the second longitudinal portions 210 ga, 219 gb form source/drain regions in the FINFET 300. The lower portion 210 b under the upper portion 210 a has a base 210 e and bottom-up tapered sidewalls.

Referring to the cross sectional view of FIG. 3C taken along the line c-c of FIG. 3A, the gate structure 320 comprises the gate electrode 320 a and the gate insulator 320 b. The gate electrode 320 a is disposed over the gate insulator 320 b. If the thickness of the gate insulator 320 b is uniform on all the surfaces of the fin structures 210, a triple gate transistor is formed. The channel 330 of the triple gate transistor is disposed under the gate structure 320 and within the top surface 210 c and sidewalls of the third longitudinal portion 210 gc of the upper portion 210 a of the fin structures 210. However, in some embodiments, an additional dielectric layer (not shown) may be formed over the top surface 210 c of the third longitudinal portion 210 gc of the upper portion 210 a before or after forming the gate insulator 310, the channel 330 of the FINFET 300 is formed only along the sidewalls of the third longitudinal portion 210 gc, forming a double gate transistor.

FIG. 3D illustrates a cross-sectional view of the FINFET 300 taken along the line d-d of FIG. 3A. The fin structures 210 disposed between the isolation structures 220 are extending in a longitudinal direction 210 g and continuous pieces of the underlying substrate 202. In some embodiments, the fin structures 210 may be separated from the substrate 202 by an insulation layer (not shown). In some embodiments, the first and the second longitudinal portions 210 ga, 210 gb of the upper portion 210 a of the fin structures 210 comprise dopant-rich regions (not shown), and a silicide layer (not shown) may be disposed within the first and the second longitudinal portions 210 ga, 210 gb forming source/drain regions 329 a and 329 b in the FINFET 300. In various embodiments, the thickness of the dopant-rich regions is about 0.5 nm to about 10 nm. Then, subsequent processes, including interconnect processing, must be performed after forming the FINFET 300 to complete the IC fabrication.

While the invention has been described by way of example and in terms of the preferred embodiments, it is to be understood that the invention is not limited to the disclosed embodiments. To the contrary, it is intended to cover various modifications and similar arrangements (as would be apparent to those skilled in the art). Therefore, the scope of the appended claims should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements. The invention can be used to form or fabricate a fin structure for a FINFET having no isolation recess. 

What is claimed is:
 1. A method of fabricating a semiconductor device comprising: forming a patterned hard mask layer over a substrate; using the patterned hard mask layer as a masking element during a first etch process of the substrate to form an upper portion of a fin structure; thereafter, using the patterned hard mask layer as the masking element during a second etch process of the substrate, wherein the second etch process includes at least one parameter different than the first etch process; and forming a dielectric layer adjacent the fin structure, wherein a top surface of the dielectric layer is coplanar with the upper portion of the fin structure.
 2. The method of claim 1, wherein the at least one parameter different is bias power.
 3. The method of claim 2, wherein the first etching process has a first bias power lower than a second bias power of the second etch process.
 4. The method of claim 1, wherein the at least one parameter different includes source power, wherein the second etch process has a greater source power than the first etch process.
 5. The method of claim 1, wherein the at least one parameter different includes providing a different group of etching gases.
 6. The method of claim 5, wherein the first etching process includes CH₂F₂, SF₆, N₂ and He as etching gases and the second etching process includes HBr, SF₆, and He as etching gases.
 7. The method of claim 5, wherein the first etching process includes CH₂F₂ as an etching gas and the second etching process includes HBr as an etching gas.
 8. The method of claim 1, wherein the first etching process forms an upper portion of the fin structure having a substantially constant first width from a top surface of the fin structure to a transition location; wherein the second etching process forms a lower portion of the fin structure having tapered sidewalls from the transition location to a surface of the substrate, wherein the tapered sidewalls of the lower portion define a second width proximate the surface of the substrate, the second width greater than the first width.
 9. A method of fabricating a semiconductor device, comprising: providing a substrate; performing a first etch process to etch the substrate to form an upper portion of each of a first fin and an adjacent second fin, wherein the upper portion has a substantially vertical sidewall; stopping the first etch process and performing a second etch process to etch the substrate to form a lower portion of each of the first and second fins, wherein the lower portion is contiguous with the upper portion and includes a slope that continually decreases from an interface with the upper portion to the substrate; filling a space between the first and second fins with a dielectric material, wherein the dielectric material disposed on the upper and lower portions of the first and second fins; and removing a portion of the dielectric material to expose a region of the upper portions of the first and second fins.
 10. The method of claim 9, wherein the first etch process includes a first bias power and the second etch process includes a second bias power, the first bias power being lower than the second bias power.
 11. The method of claim 9, wherein the first etch process includes a first source power and the second etch process includes a second source power, the first source power being less than the second source power.
 12. The method of claim 9, wherein the slope that continually decreases from the interface with the upper portion to the substrate is disposed at an angle between approximately 60 and 85 degrees to a top surface of the substrate.
 13. The method of claim 9, further comprising: forming a gate structure over the regions of the upper portions of the first and second fins.
 14. The method of claim 9, further comprising: forming a hard mask layer over the substrate; and patterning the hard mask layer to define a pattern of the first and second fins.
 15. The method of claim 14, wherein patterned hard mask layer is disposed on the substrate during the first and second etching processes.
 16. A method of fabricating a semiconductor device, comprising: forming a fin structure on a semiconductor substrate, wherein the forming the fin structure includes: performing a first etch having a first source power, a first bias power, and a first etching gas composition; and after performing the first etch, performing a second etch having a second source power, a second bias power, and a second etching gas composition, wherein the second source power is different than the first source power, the second bias power is different than the first bias power, and the second etching gas composition is different than the first etching gas composition; and forming a gate structure over the fin structure.
 17. The method of claim 16, wherein the first etch forms a portion of the fin structure having substantially vertical sidewalls and the second etch forms a portion of the fins structure having tapered sidewalls.
 18. The method of claim 17, wherein the substantially vertical sidewalls and the tapered sidewalls interface at a point on fin structure.
 19. The method of claim 16, further comprising; depositing an insulating material adjacent the fin structure after the first and second etch and prior to forming the gate structure.
 20. The method of claim 16, wherein the second etching gas composition includes HBr and the first etching gas composition includes CH₂F₂. 